Re: [MW:26806] Tensile strength for PQR qualification of ASTM A519 Gr4130 material

It is normalised, Q&T. For stress relieving, follow manufacturers recommendation

On 10-Sep-2017 6:20 pm, "Aby Jose" <abycscec@gmail.com> wrote:
Boxbe This message is eligible for Automatic Cleanup! (abycscec@gmail.com) Add cleanup rule | More info

Dear experts,

I am conducting a PQR for ASTM A 519 Gr 4130 QT pipe material.When I checked A519 standard it is giving the tensile strength values for 4 conditions only. Hot rolled/stress relieved/Annealed/Normalised.But in the material mtc I cannot find any details regarding the condition. It is given as Quench tempered only. The UTS of the parent material in mtc is 728mpa.

 As per PWPS  I have done PWHT after welding. When I did the tensile test ; ductile fracture occured in the parent material with a UTS of 683. 

What is the minimum tensile strength required for the PQR to get accepted?

Regards,
Jose


--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...