you could use a "B2" filler metal. The next issue in filler metal selection is the use of post weld stress
relief which is not mentioned. If the weld is going to be subjected to a post weld stress relief then use
an ER80S-B2 and if there will be no post weld stress relief you should consider ER70S-B2L.
Regards,
C Sridhar.
Technical Adviser - Welding,
for Alsta Pristine Engineering Private Limited,. Bangalore
( SS, AL fabricators & A venture of Advance Eng. Training & Inspection Services). Chennai,
Mobile nos: 0 94449 71097,
C Sridhar.
Technical Adviser - Welding,
for Alsta Pristine Engineering Private Limited,. Bangalore
( SS, AL fabricators & A venture of Advance Eng. Training & Inspection Services). Chennai,
Mobile nos: 0 94449 71097,
Please don't print this e-mail unless you really need to. Save the environment.
From: 'nawab ali bhatti' via Materials & Welding <materials-welding@googlegroups.com>
To: "materials-welding@googlegroups.com" <materials-welding@googlegroups.com>
Sent: Thursday, 11 February 2016 8:09 PM
Subject: [MW:24268] Alloy Material P22, A335 (Cr2.25 and Mo 1)
Dear Experts
Please share your best experience with reference of international codes
Pipe Material P22, A335 (Cr2.25 and Mo 1), Shoe support to be welded direct with pressure parts.(Pipe material thickness 33 mm, Operating Temperature 500 Centigrade and pressure 106 bar)
My question, Is PWHT require for shoe supports Or Not???
Shoe support plate thickness is 12 mm and throat thickness is 8 mm, Preheating is perform as WPS.
NA Bhatti
00966 593530001
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/241801168.2167526.1455201549003.JavaMail.yahoo%40mail.yahoo.com.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment