Pre-heat and PWHT as per approved or adopted PQR and WPS.
Date: Sat, 30 Jan 2016 09:59:36 +0500
Subject: [MW:24187] Hardness Of P-91 Material
From: pradipsil@gmail.com
To: materials-welding@googlegroups.com
--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAB%3DAs8mJXj9twE50bbG4-%2Bb-_35XPHeuAZ97xUD5n1Aq7TR21Q%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.
Date: Sat, 30 Jan 2016 09:59:36 +0500
Subject: [MW:24187] Hardness Of P-91 Material
From: pradipsil@gmail.com
To: materials-welding@googlegroups.com
Dear Everybody,
Some of our P-91 Joints( Weldment) are coming hardness value around 300HB in the HRSG Unit.
Joints thickness is 18 mm & 20 mm & we did PWHT 2 hours holding time at 710 degree centrigrade also we did 150 degree heating rate ,120 degree cooling rate.
Can you pls suggest us this hardness value is acceptable in the HRSG unit. If not pls suggest me how to recover.
Regards,
Kumar
--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAB%3DAs8mJXj9twE50bbG4-%2Bb-_35XPHeuAZ97xUD5n1Aq7TR21Q%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment