Re: [MW:21508] CAN WE PERFORM PWHT AFTER SS 304 CLADING/OVERLAY ON ALOY STEEL

304 clad not suitable for F5. It has to be 321 or 347 clad. vanchi

Sent from Windows Mail

From: HEMANT SUTHAR
Sent: ‎Thursday‎, ‎31‎ ‎July‎ ‎2014 ‎16‎:‎46
To: materials-welding@googlegroups.com

Dear Sir,
I have to do PWHT after explosive bonding and some portion overlay welding in heat exchanger. We have to do overlay and weld cladding of SS 304 on SA 336 Gr. F5. PWHT heating cycle is 720 C at 2 hours.

 Material : SA 336 Gr F5 + SS 304 CLAD

now my doubt is if we will do PWHT in sensitization range so that there is chance of IGC in SS material and SS clading will not fulfill its corrosin resistance purpose.
so kindly pls suggest we can do or not do???

Thanks,
Hemant Suthar
7600096712

Get your own FREE website, FREE domain & FREE mobile app with Company email.  
Know More >

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

No comments:

[MW:35346] Cast-iron welding

Any advice for cast iron welding Sent from Yahoo Mail for iPhone