The requirement for ±14 is a personal requirement. Interpretation IX-07-06 clearly defines the temperature range for ferritic materials to be restricted only to the broad groupings of QW-407.1.
John A. Henning
Welding & Materials
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Prakash Hegde
Sent: Friday, January 04, 2013 2:28 AM
To: materials-welding@googlegroups.com
Subject: Re: [MW:16430] QW407.2 (ASME Sec. IX)
Dear Mr Hussain
PWHT QW 407.2 is applicable in case of suplimentary essential i.e. When Weld has to undergo Impact test6
In this case Soaking time for Production coupon or ajob should be at least 80% of the soaking time of relevent PQR qualified And Soaking Temp should be with in 14 degree of the of the soaking temp of PQR qualified (i.e If your PQR is qualified at Soaking temp say 600-615C then your Job / Test coupon also should be heated in thyis range and Not at say above 615C Even though this temp is below AC1
Regards
Hegde P.B.
+91880559304
From: Tariq Hussain <tariqhussain632@gmail.com>
To: materials-welding@googlegroups.com
Sent: Wednesday, 2 January 2013 5:26 PM
Subject: [MW:16407] QW407.2 (ASME Sec. IX)
Dear All,
We need little help from you regarding below query for ASME Sec. IX QW-407.2
Is it intention of QW-407.2 to have Production Welds Soak Temperature (Vessel Soak temperature) exactly same as that of done in PQR test Coupon?
Thanks in Advance
Tariq Hussain
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
______________________________________________________________________
The information in this email is confidential, and is intended solely for the addressee(s). If you are not the intended recipient of this email please let us know by reply and then delete it from your system; you should not copy this message or disclose its contents to anyone. The internet can not guarantee the integrity of this message. HAMON (and its subsidiaries) shall (will) not therefore be liable for the message if modified.
______________________________________________________________________
No comments:
Post a Comment