I have faced with problem when I tried to weld it before. a HAZ was weak and most times I found a crack in the HAZ. How to avoid it? is any heat treatment required after welding?
regards,
Martin.
Date: Fri, 1 Apr 2011 09:19:41 +0700
Subject: Re: [MW:10551] WELD DETAIL FOR WELDING OF AL 6082-T6
From: karthik14475@gmail.com
To: materials-welding@googlegroups.com
You can use ER4043
Regards,
(Karthik)
On Thu, Mar 31, 2011 at 6:43 PM, Martin Prad <martin_prad@hotmail.com> wrote:
Dear Friends,
Could you please advise some details (welding consumable+elecrtricial detail) for welding of aluminum grade 6082-T6?
Your valuable inputs will be highly appreciated.
Thanks,
Martin.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment