[MW:2010] Re: effect of H on notch strength

hi chaps

do you say ,the notch strength is similar to tensile strength?if it is true,why tha strength in 200 is more than 50?

rjd

---

From: babu k <kbabupsg@gmail.com>
To: materials-welding@googlegroups.com
Sent: Tuesday, April 21, 2009 6:43:28 PM
Subject: [MW:2000] Re: effect of H on notch strength

Chaps,

 

Please find the attachment, hopefully clarify the things,

 

 

On Tue, Apr 21, 2009 at 7:36 PM, Ali Asghari <asghariali@rocketmail.com> wrote:

hi oven

thank you for answer,but i dont understand yet.

because the toughness in -100 is more than in 50,why?

another question:this figure is true in all steel?

regard advance

---

From: Owen Jenkins <owen@osjl.co.uk>

To: materials-welding@googlegroups.com

Sent: Sunday, April 19, 2009 12:20:17 PM
Subject: [MW:1985] Re: effect of H on notch strength

Ali,

The top line shows the toughness of the base material without hydrogen embrittlement occurring - toughness increases steadily with increasing temperature.

 

The lower, V-shaped line shows that the effect of hydrogen embrittlement is worst at about 50°C, decreasing rapidly as the temperature increases (and the ability of the hydrogen to diffuse out of the metal increases) and also decreasing at lower temperatures, where reaction rates are much lower and the density of hydrogen increases, hence its volume decreases.

 

Other may wish to add more to this simple approach. Does this help?

 

Regards,

Owen.

----- Original Message -----

From: Ali Asghari

To: materials-welding@googlegroups.com

Sent: Saturday, April 18, 2009 11:31 AM

Subject: [MW:1980] effect of H on notch strength

hi

can anybody explain about this picture?

rgds.

---

--
Thanks & regards,

K.Babu
Welding Engineer,
PPL Shipyard Pte Ltd
Singapore
HP:  +65 94815990
Skype: psgbabu



--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---