[MW:1253] RE: 1250] Re: HAZ

Dear Shailesh,

 

As everybody informed that HAZ is largely depend on the process and other parameter is correct but my experience HAZ in manual welding is less than 3 mm and Auto (SAW and other high heat input process) it will be less than 5 mm for carbon steel and LAS. For SS I have not observed HAZ bigger than 1 mm (we can see after etching too).

 

I hope experienced people like Mr Kalayan can comment on statement as he might have seen many cross section HAZ after etching…..

 

Regards.

 

C. K. Purohit 

General Manager

QA / QC / WELDING / NDT / R&D

KNM Process Systems Sdn Bhd - Malaysia

 

HP - +6016 337 6448

 

 

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Kalyan Elcalabs
Sent: Sel, 28 Okt 08 02:42 pm
To: materials-welding@googlegroups.com
Subject: [MW:1250] Re: HAZ

 

Dear Shailesh,

 

There is no thumb rule for the formation of HAZ. This largely depends on welding procedure, equipment used, various consumables, electrical parameters, operators skill and the uncertainities contributed by them. Normally one should expect minimum HAZ as is it not a desirable phenomena in any welding process.

 

N. Kalyan.

ELCA Laboratories.

 

 

----- Original Message -----

From: shailesh dave

To: materials-welding@googlegroups.com

Sent: Monday, October 27, 2008 6:53 PM

Subject: [MW:1247] Re: HAZ

 

DEAR SACHIN,   LET ME MAKE MY QUESTION CLEAR TO YOU. FROM WELD JOINT END HOW MUCH IS THE WIDTH OF HAZ.   REGARDS,   SHAILESH --- On Mon, 10/27/08, sachin sankhe <sachin.sankhe@rediffmail.com> wrote: From: sachin sankhe <sachin.sankhe@rediffmail.com> Subject: [MW:1246] Re: HAZ To: materials-welding@googlegroups.com Date: Monday, October 27, 2008, 5:34 PM Hi Shailesh Your question is not clear Regards Sachin On Sat, 25 Oct 2008 shailesh dave wrote : >DEAR MEMBERS, > >WOULD YOU PLEASE TELL ME WHAT COULD ME THE THUMB RULE FOR HEAT AFFECTD ZONE DURING WELDING. > >REGARDS, > >S.N.DAVE >I/C QA/QC DAS ISLAND UAE > > > >>   <BR

 

***DISCLAIMER NOTICE ***
"This e-mail and any files transmitted with it is confidential and is intended only for the use of the recepient(s) named above.
If you are not the intended recipient, any review, retransmission, dissemination, distribution, printing, copying or use the information contained in this message or any part thereof in other manner is strictly prohibited.
If you receive this e-mail in error, please notify the sender immediately by return e-mail and delete the e-mail and any of its attachments.
Any personal views or opinions expressed by the sender shall be understood as neither given nor endorsed by KNM or any of the companies within the Group."

--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---