Dear Friend
ASTM A 148 is a ferritic-pearlitic carbon steel for cast products. It is used for higher pressures and stress parts like crane wheels,etc..
I think the chemical composition is C=0.4-0.5, Mn=0.4-0.8, Si=0.2-0.5,P&S=max.0.090.
First you should arrest the crack by drilling two holes,remove the crack by hand grinding, ensure crack removal by LPT.
Preheat the job to 250 degrees celcius, Use E7018-1 electrodes,Interpass temp of 250 degrees celcius and weld. After welding cover the job with asbestos cloth for slow cooling.
I am suggesting you this procedure because we had repaired one cast steel of similar composition in the past.
Any suggestions / expert comments are welcome...
Cheers
Prem Nautiyal
Godrej, Mumbai
Cell: 9820313278
On Sun, 12 Oct 2008 greetings wrote :
>Friends,
> Crack observed in casting material ASTM A 148 GR 80-40
>Can any one give the process to rectify the crack (welding electrode,Preheat
>Temp & etc)
>
>Regards
>DST
>
>>
PREM S NAUTIYAL
CELL : 9820313278
 |
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---
Popular posts from this blog
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
If weep hole is not provided in dummy pipe before welding
What will happen???
--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com .
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/da251ee6-fa7f-4851-b876-cdb3834ae341%40googlegroups.com .
Dear Experts, Can anyone share the inspection requirements or a qualification procedure for cold bending? Our client spec states only the requirements for induction bending and would like to know your opinion on the cold bend inspection requirements. The code of construction is B31.3, Max. 5D bends, A106 SS 316L. Thanks in Advance. -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion visit https://groups.google.com/d/msgid/materials-welding/1be61cc3-e9c9-4a5f-834d-e8485e248432n%40googlegroups.com .
Comments