if you look for for a thumb rule about haz that it is used in each situation ,it not exist.
but i prefer some following below,considered:
chemical analysis of parent metal(carbon equivalent)
thickness of parent
H.I & preheat depends on process
joint design
if you express a special case,i can help more detail
bye
if you look for for a thumb rule about haz that it is used in each situation ,it not exist.
but i prefer some following below,considered:
chemical analysis of parent metal(carbon equivalent)
thickness of parent
H.I & preheat depends on process
joint design
if you express a special case,i can help more detail
bye
From: shailesh dave <snd2988@yahoo.com>
To: materials-welding@googlegroups.com
Sent: Saturday, October 25, 2008 12:44:10 PM
Subject: [MW:1244] HAZ
DEAR MEMBERS, WOULD YOU PLEASE TELL ME WHAT COULD ME THE THUMB RULE FOR HEAT AFFECTD ZONE DURING WELDING. REGARDS, S.N.DAVE I/C QA/QC DAS ISLAND UAE |
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---
No comments:
Post a Comment