[MW:1217] RE: 1216] Re: How to reduce the exposure time for RT

is there any advantage using copper or composite screens?
-----Original Message-----
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com]On Behalf Of raghavendra pemmaraju
Sent: Thursday, October 16, 2008 5:35 PM
To: materials-welding@googlegroups.com
Subject: [MW:1216] Re: How to reduce the exposure time for RT

Dear CKP,
you can use combination of two sources together ( unsharpness is not an issue since the thickness is 100mm and SFD 2m) this will increase the Curie strength of the source.
Also while developing you may increase the Temperature of the developer to 2 deg.C sothat an imporvement of 0.2 H&D of optical density can be had, proportionately you can reduce the exposure time. When you use Combination of films ( double film with minimum optical density of 1.3H&D per film), you are in tern effectively reducing the exposure time by 40% when compared to that of a single film with 2.0H&D optical density.
 
you can even try to use high speed films such as AGFA D8 provided you are achieving the required sensitivity. This will reduce further 30% of exposure time.
Try the above remedies, all the best !
 
regards,
 
RPE

--- On Thu, 10/16/08, CKPurohit <ck@knm-group.com> wrote:
From: CKPurohit <ck@knm-group.com>
Subject: [MW:1215] How to reduce the exposure time for RT
To: materials-welding@googlegroups.com
Date: Thursday, October 16, 2008, 7:04 PM

Dear Group,

 

I need help to find out how to reduce the exposure time for heavy wall thickness RT (above 4" thickness and ID of vessels 4 meter) .

 

Composite film is one of the option. Any other idea ?

 

I heard from my client that there are accelerators available which can be used for developing the film to compensate the reduce time of exposure.

 

We are using Co-60.

 

Regards.

CK


***DISCLAIMER NOTICE ***
"This e-mail and any files transmitted with it is confidential and is intended only for the use of the recepient(s) named above.
If you are not the intended recipient, any review, retransmission, dissemination, distribution, printing, copying or use the information contained in this message or any part thereof in other manner is strictly prohibited.
If you receive this e-mail in error, please notify the sender immediately by return e-mail and delete the e-mail and any of its attachments.
Any personal views or opinions expressed by the sender shall be understood as neither given nor endorsed by KNM or any of the companies within the Group."


--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

By -

No comments:

Post a Comment

Subscribe to: Post Comments (Atom)

[MW:34919] Welder qualification certificate

Dear All     anyone can share a format for welder certificate and card format        Thanks & Best Regards Saleem manhappulath Mob:+9665...

  • Materails FAQs
    Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
  • RE: [MW:5585] Buttering of weld joints
    Definition of buttering from ASME Section IX, QW/QB-492 Definitions:   Buttering:  the addition of material, by welding, on one or bot...
  • WELD AND WELDING SYMBOLS
    Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...
CONFIDENTIALITY NOTICE
This e-mail and any attachments there to contain information, which is confidential, proprietary, privileged and/or protected from disclosure by intellectual property rights and are intended for the sole use of the recipient(s) named above. If you are not the intended recipient of this message you are hereby notified that any dissemination or copying of this message is strictly prohibited. If you have received this e-mail in error, please notify the sender either by telephone or by e-mail and delete it from any computer. Although this e-mail and any attachments thereto are believed to be free from any virus or other defects, which might affect any computer or IT system, it is the responsibility of the recipient to ensure that they are virus free. We are not liable for any loss or damage arising in any way from receipt or use there of. Thank you.

Pages

Contributors

Blog Archive