Re: [MW:34367] Re: Which Filler wire to be used in between P43 (Inconel 625) to P8 (A240 310S) by GTAW)

Greetings,

Please share WPS sample for P43 to P8 welding.

ASME Sec. ix.

Muhammad Babur Khan

Sent from my iPhone

On 24 Nov 2021, at 12:31 PM, Kannayeram Gnanapandithan <kgpandithan@gmail.com> wrote:

Why Inconel 625 is not suitable, could you elaborate to understand.

THANKS & BEST REGARDS,
KG.PANDITHAN, BE, IWE, CSWIP 3.1,
ISO 9712 Level 2 in VT,
ASNT-Level II in PT,MT,RT & UT,
LA ISO 9001-2015,
International Welding Engineer.
CONSULTANT-WELDING & QUALITY
Mobile no: +919940739349

On Wed, Nov 24, 2021 at 1:39 PM Arun Padman <arunpadman0105@gmail.com> wrote:
Dear,

ER NiCrMo-3 is suitable to weld 625 to 600/625/825/C-22/B-2 etc., not 310.

Regards,

Arun Padman Manayil
P Save a tree. Please don't print this e-mail unless you really need to

On Wed, Nov 24, 2021 at 6:19 AM rahmat khan <mkrahmat11730@gmail.com> wrote:
As per my understanding For P43 Filler wire ER NiCrMo-3 is suitable as per chemical and mechanical properties.

On Tuesday, November 23, 2021 at 2:14:21 PM UTC+5:30 rahmat khan wrote:
Dear All,

Please help me with this:

1) which filler wire is to be used for GTAW welding of two dissimilar materials P number that is P43 (Inconel 625) to P8 (A240 310S).

2) For SA 516 Gr 70 22mm thick. Ellipsoidal 2:1 dish end, which heat treatment to be used as per ASME Sec VIII Div I UCS 56 After cold forming of dish end.

Please help me I this?

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/3e2b21db-9755-4cba-8aca-e91531d1f0f9n%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAHbaPvJ9FOAOW%3DTz_isdOZcLtikfYDWJQo5mu6_1gVdpLokHng%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJzm4eNEYwgXEmNErqwosZkqd5LGqDK%2BFLhTxrFEs6L0DSPmrw%40mail.gmail.com.

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Re: [MW:10788] ON PLOT PIPING & OFF PLOT PIPING

Piping systems involved for the flow lines and gathering lines from the well head isolation valve to the production facility or processing plant isolation valve are determined as OFF PLOT. ON PLOT defines piping system in the processing plant and production platform. ANSI/ASME B31.4 applies for off plot piping system. B31.4 allows the use of either API 1104 or ASME section IX (as appropriate). However, occasionally, a very small system such as piping within 500 feet of a processing plant (some client also said 400 feet) may be declared B31.3 rather than B31.4. When B31.3 is invoked, only ASME Section IX is used. before you decide which code to use for welding procedure and/or welder qualification for pipe welding, you have to know the design and construction code applicable to the system. Please read far enough into scope and diagram illustrating the application of either B31.3 and B31.4 hope this helps rgds 2011/4/21 pradip kumar sil < pradipsil@gmail.com > Dear all, ...

Materials & Welding

Search This Blog