Re: [MW:33756] SS PIPE ASTM 554 TYPE 304

Dear Expert.

Thank you for your information,

If we will use 316L filler wire what is the effect for welding?

On Mon, Nov 21, 2022 at 9:56 AM Kannayeram Gnanapandithan <kgpandithan@gmail.com> wrote:

308
THANKS & BEST REGARDS,
KG.PANDITHAN, BE, IWE, CSWIP 3.1,
ISO 9712 Level 2 in VT,
ASNT-Level II in PT,MT,RT & UT,
LA ISO 9001-2015,
International Welding Engineer.
CONSULTANT-WELDING & QUALITY
Mobile no: +919940739349

On Sat, Nov 12, 2022 at 6:38 PM Simhachalam Battini <simhachalam.battini729@gmail.com> wrote:
Dear All,

Great to hear from you.

Which filler is required to weld ss Pipe to Pipe ASTM A554 Type 304.

Thanks, Regards.

Battini Simhachalam

QC Inspector – Quality Dept.

ArRiyadh New Mobility - CWG

6^th Floor, ArRiyadh New Mobility Building

Olaya Street (North) – Al Sahafah District

P.O. Box 99816 – Riyadh 11625 – Saudi Arabia

M +966 546044327

simhachalam.battini@cwg-metro.com

www.anm-metro.com

24°46'57.42"N 46°38'26.10"E

Location map (click here)

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CABk4cbF476CBNYD5%2By1NJAYOZVXZKFNWe0tuiV%2B1SV%2BipuhwMw%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJzm4eMmYQPpj3B9gcbVG6QQ8sfiKH3y7L4hRxLzZWUEDi67gg%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CABk4cbEbx2x%2BXXcRV8rawGyXhUAWwvGfajsLoBpoUjx_RWpF%2Bw%40mail.gmail.com.

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

[MW:5202] RE: 5200] NDT after PWHT

------------------------------------- Interpretation: I‑89‑14 Subject: Section I (1986 Edition, 1987 Addenda), PW‑11, NDE Prior to PWHT Date Issued: December 15, 1988 File: BC88‑393 Question: Does PW‑11 require that NDE be performed on welds after they have been subjected to the postweld heat treatment required by PW‑39? Reply: No, unless the conditions described in PW‑11.2.2 exist. ---------------------------------------------- Interpretation: VIII-1-98-09 Subject: Section VIII, Division 1 (1995 Edition, 1996 Addenda); NDE ...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Materials & Welding

Search This Blog