Re: [MW:33663] Re: E 7018 or E 7018-1

pl see A6.4,  A 6.5.1 & 6.5.2

THANKS & BEST REGARDS,

KG.PANDITHAN, BE, IWE,  CSWIP 3.1,

ISO 9712 Level 2 in VT,

ASNT-Level II in PT,MT,RT & UT,

LA ISO 9001-2015,

International Welding Engineer. 

CONSULTANT-WELDING & QUALITY

Mobile no: +919940739349

On Thu, Nov 3, 2022 at 11:02 AM 'james gerald' via Materials & Welding <materials-welding@googlegroups.com> wrote:

Job thickness will give the requirement of Impact test if applicable.

Thanks & Regards

J.Gerald Jayakumar

On Thursday, 3 November, 2022 at 10:16:13 am IST, sujit kumar <sujitkumar19942@gmail.com> wrote:

E-7018 Elextrode is acceptable for SA516 Gr 70 

Plese, ensure the electrode should be impact tested at -29 degrees. It will be available in MTC of the electrode.

Best Regards

Sujit kumar.

On Thu, 3 Nov 2022 at 09:24, Vishwas Keskar Welding Manager WELDING <vvkeskar123@gmail.com> wrote:

E7018 shall satisfy the requirement.

Pl ensure that the electrode batch is tested for  above   conditions mentioned by you .

Get the Welding Consumable Manufacturers confirmation .

Thanks 

Vishwas -IWE

International Welding Engineer

On Thursday, November 3, 2022 at 8:49:24 AM UTC+5:30 williamswilsonp wrote:

Dear Experts,

Greetings to all.

Could you please suggest suitable SMAW welding electrode (E 7018 or E 7018-1) for the below specifications,

MOC                                                   : SA 516 Gr.70 + N , 70 mm Thickness

PWHT                                                 :  610 ° C x 300 minutes minimum

Impact Test after HT                             :  -29° C

Weld Metal & HAZ Hardness (Max.) : 22 HRC

Thank You & Regards

Williams P Wilson

+968-94600828

QA/QC Engineer

Please consider the environment before printing this message

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/38186434-76bd-404f-bd99-0ef9184851b1n%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAFonYWMysXUw7qrKWYZy859P_AUh7OfiMzSjCOY7VCtN8i_rVw%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/92255972.1829396.1667452958216%40mail.yahoo.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJzm4eNb1RoXy_%3DMEGEy3noJ5Pz8E51eN4ryxF1or8iNmLQX0w%40mail.gmail.com.