Re: [MW:31233] Combination of PQRs

Hi KK,
Your procedure is qualified as per ASME section IX, qualification procedure part is completed.
This is an additional project requirement, it has nothing to do with procedure qualification so you can make a coupon and test for HIC as per project specification as per NACE TM-0284 like corrosion tests or any test other than required as per ASME Section IX.

On Tue, Jul 28, 2020 at 11:02 AM K K <karan.hbl@gmail.com> wrote:
Hi,

Yes, Piping requirements.

SA 516 gr 60/70. and according to ASME Sec.IX and ASME B31.3.
The main PQR is qualified with PWHT, but not HIC tested.
And I have additional PQR with HIC tested, but not qualified with PWHT, and no other lab test reports like a mechanical test, bend test, and hardness test report, shall I combined this PQR to my WPS.

Please looking you feedback.
Thanks 
Kiran



On Tuesday, July 28, 2020 at 10:12:01 AM UTC+5:30, Sudhakar Kuppuswamy wrote:
Hi,

Please specify the material grade and the design code. 

As you have mentioned Line class, I presume you are talking about piping . 

Regards 
Sudhakar K 

On Mon, 27 Jul 2020 at 11:33 AM, K K <kara...@gmail.com> wrote:

Hi Experts,


"Good Morning"


According to my line classes, I required NACE+HIC+PWHT Wet H2 services.

What is the test shall be conducted according to the standard to meet the requirements?


I have one PQR with NACE+PWHT+Wet H2S services, but not HIC test.

In addition, I have qualified one HIC tested PQR without PWHT no other lab test certificates, shall I combined this PQR to the above requirements( NACE+HIC+PWHT+wet H2S).

For your information, the HIC test is an additional requirement of our specifications.

Please looking your feedback on my above query.


Thanks and Regards

Kiran

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to material...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/f1d53635-4e0f-4fe5-a0cf-ec93a8d2d87bo%40googlegroups.com.
--

Regards,

Sudhakar K CEng MWeldI,IWE.

Welding & Metallurgical Engineer,

Email: sudhak...@gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/036721c7-5728-4727-b92a-ad48067f8453o%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CACgUO5mmfoqNLK4fa32398Sp7WszFYBOzTs-fpOa6WtGiCDQHw%40mail.gmail.com.

No comments:

[MW:35346] Cast-iron welding

Any advice for cast iron welding Sent from Yahoo Mail for iPhone