Dear Venkat , minor transvers crack shouldnot be an issue . This is a generic with some hardfacing consumable.
On Wed 1 May, 2019, 12:15 Chintan, <chintan51@gmail.com> wrote:
Apply ss 316L as buffer layer thickness 2 mm
Then grind / machine the component to have uniform 2 mm buffer layer on whole assembly
Preheat 100 deg cel interpass 175 deg cel
Do not over heat base metal, temp shuold not cross 200 deg cel in any case
Apply pta powder
SLOW COOLING TO ROOM TEMPRATURE BY wraping in fire blanket
( if possible to replace pta by gmaw then use ERCocr-a wire for better result)
--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment