NACT or Norm and Temp. both ok
if mechanical properties are within acceptable limit after HT.
Adviced to simulate HT on test coupon and carry out mechanical tests. Then decide final HT on componant.
Regards,
Prasad G.
On Tue, 26 Jun 2018 16:07 Jayesh Parekh, <jayeshparekh34@gmail.com> wrote:
i purchase SA387 plate in NACT condition. But in my fabrication process i have to give one intermediate normalizing. So, this intermediate normalizing cycle also follow NACT cycle ? Or i only normalized and then tempered material, it will ok or Not ?--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment