Hello,--I need help regarding the ER70S-6 mig welding wire. I am currently comparing mill certs from different vendors and not sure which one is the best in terms of quality. Is there anything in particular I should be looking for?Any help would be greatly appreciated!On Tuesday, September 20, 2016 at 6:50:21 AM UTC-5, Diganta Sarma wrote:Ti and Al are added to act as additional deoxidizers to cleanse the weld of impurities. In the case of MAG welding, additional Ti and Al into the standard ER70S-6 isn't mandated. In case you need them in the weld pool, consider changing the transfer mode to spray or rotating arc or pulsed mode. Some of these will require change of gas to a Argon based mixture
Many thanks!
Sent from my iPhonein ER70S6 we have added Ti- 0.011% and Al - 0.012%. We are facing spattering issue in MAG-CO2 .--Is Ti and Al reason for spattering?
Sanjeev
On Saturday, 17 September 2016 17:39:35 UTC+5:30, sridhar wrote:You have not mentioned the welding process in use at your end
If it is TIG, flat no. as 70 S2 contains triple deoxidisers Al, ZN & Ti and used with argon gas.ER 70S06 does not have them and will not give x-ray quality welds.
If it is MAG/CO2 process or with argon gas, you can go ahead.
Ti addition alone with 70 S6 do not help. S6 also contains excessive Mn & Si and not used forTIG process.
Sridhar.
From: sanjeev singh <sanjeev...@gmail.com>
To: Materials & Welding <material...@googlegroups.com>
Sent: Thursday, 15 September 2016 11:40 AM
Subject: [MW:25396] Re: Using of ER70S-6 in place of ER70S-2
Please guide- If we add Ti in ER70S-6 in range of 0.011%, what will be the effect during CO2 welding?--
regards,
Sanjeev
On Thursday, 10 January 2013 12:13:36 UTC+5:30, Ranendra Chakraborty wrote:Dear Expert,Please guide whether ER70S-6 can be used in place of ER70S-2. Please give code reference.Regards,Ranendra
http://www.linkedin.com/groups/MaterialsWelding- 122787?home=&gid=122787&trk= anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com .
To post to this group, send email to materials-welding@googlegroups.com .
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/ .07c21334-a631-40b0-b66e- 65075cde9914%40googlegroups. com
For more options, visit https://groups.google.com/d/optout .
http://www.linkedin.com/groups/MaterialsWelding- 122787?home=&gid=122787&trk= anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com .
To post to this group, send email to material...@googlegroups.com .
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/ .52b79f3f-41b6-475b-8d52- c277ae280bfd%40googlegroups. com
For more options, visit https://groups.google.com/d/optout .
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment