Re: [MW:26628] Hardness Test On A106 Gr B / C Material

341.5.2 Hardness Tests. Hardness tests are not
required to verify proper heat treatment except as otherwise specified in the engineering design.
ASME B31.3-2016

Carlos Arturo Oliveros Diaz +573023482020

ws+584245923932

De: materials-welding@googlegroups.com <materials-welding@googlegroups.com> en nombre de ΓΙΩΡΓΟΣ GEORGIOS D. <dilintas@gmail.com>
Enviado: martes, 20 de junio de 2017 8:36 a. m.
Para: materials-welding@googlegroups.com
Asunto: Re: [MW:26625] Hardness Test On A106 Gr B / C Material

You will not find in 31.1.

We may look in 31.3 as a guidance

Sent from my Samsung Galaxy smartphone.

-------- Original message --------

From: Zakaria ghrab <zakaria.ghrab@gmail.com>

Date: 19/06/2017 17:33 (GMT+04:00)

To: materials-welding@googlegroups.com

Subject: Re: [MW:26624] Hardness Test On A106 Gr B / C Material

Reference please.

2017-06-19 12:20 GMT+00:00 Mahek Shah <mahekshah03@gmail.com>:

197 HRB

On Mon, Jun 19, 2017 at 2:14 PM, Zakaria ghrab <zakaria.ghrab@gmail.com> wrote:

Dear all,

please, could you give us reference from code for Hardness Test acceptance criteria for Base material, HAZ and Weld material for A106 Gr B and C.

Construction code: ASME B31.1

Thank you.

--

Thanks and Regards,

-----
زكرياء غراب
GHRAB Zakaria

Yesterday is the past, tomorrow is the future; and today? Today is the present, the gift: Enjoy it!

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

Thanks and Regards, ?

-----

زكرياء غراب
GHRAB Zakaria

Tunisia : +216 96 635 805

Morocco : +212 6 06 58 88 56

Bénin : +229 97 128 387

Yesterday is the past, tomorrow is the future; and today? Today is the present, the gift: Enjoy it!

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...

Materials & Welding

Search This Blog