you have got the answer, it is exempted from impact
-- On 13 February 2015 at 04:49, Mohit Aggarwal <aggarwalmohit05@gmail.com> wrote:
Dear Sir,
In 2.5 mm thk of base metal if you take, is it possible to do impact testing after final machining.As per Ug-84, Impact specimen can't be make from 2.5 mm thk!Best Regards,
Mohit Aggarwal.On 10-Feb-2015 9:17 am, "Raghuram Bathula" <raghurambathula@gmail.com> wrote:Q1: since full mechanical tests are not done on 5mm coupon, the combination will qualify from 5mm and not 2.5mm (QW451.1)--On 9 February 2015 at 21:38, 'Ahmed Husain' via Materials & Welding <materials-welding@googlegroups.com> wrote:Dear All,I have one query regarding below ASME IX interpretation.How come this three PQR jointly will support a WPS with notch toughness test for thickness 4.8 mm to 57 mm? if your answer is also yes, than why answer is No for first question?Appreciate your expert reply.A.H. Sidd
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CADxVub%3DeVO%3DJ65Bw7qFgDUj5PTa_OpHQw-ud2A89uJ6L4Ang4g%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment