[MW:6583] RE: Nozzle weld as per UW16.1 figure f-4 (weld metal build up)

ASME VIII code does not provide such provision. Further, this type of joint is mainly provided for item in cyclic service (mainly by Licensor) to avoid the peak stresses at the nozzle to shell junction.

 

If weld buildup is used,  that junction area is already having residual stresses, further the grain orientation which we obtain through the forged saddle type nozzle can not be achieved by weld buildup.

 

In my opinion, it has to be forged construction only. Members may please further share their experience.

 

Best Regards,

Sunil Agrawal

TICB/ +91 9820658733

 

From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Bathula Raghuram (Mumbai - PIPING)
Sent: Thursday, August 19, 2010 11:14 AM
To: 'materials-welding@googlegroups.com'
Subject: [MW:6580] Nozzle weld as per UW16.1 figure f-4 (weld metal build up)

 

 

When a lip type joint is specified as per ASME Sec VIII div 1,   UW16.1 figure  f-4 (as below), can the lip be made with weld metal buildup?

 

 


--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.


No comments:

[MW:34916] Applicability of Impact requirement as per ASME B31.3

Dear All, Design code – ASME B31.3, Welding Code- ASME BPVC SEC IX Material  to be used used during Fabrication - SA 333Gr6 (P No.1 G...