RE: [MW:32197] SM490A weld to railway

Dear Sir,

 

Enclosed material properties of railway material, while SM490A is ordinary mild steel with low carbon content <0.3%

Along I have enclosed picture of the crack.

 

1^st picture was without preheat, while 2^nd picture was with preheat 230degC & postheating 250degC x1hr.

However, crack still occurs. I'm bit lost at this point.

 

Sent from Mail for Windows 10

 

From: Vishwas Keskar
Sent: Thursday, 8 April, 2021 8:04 PM
To: materials-welding@googlegroups.com
Subject: Re: [MW:32191] SM490A weld to railway

 

Pl. send MTCs of both the materials 

 

On Thu, Apr 8, 2021 at 2:51 PM Pravin Poornachandran <htcispravin@gmail.com> wrote:

Dear Expert,

 

We are doing a weld joint with following base metal combination: 

SM490 weld to railway (alloyed, high tensile material) 

 

I used E7016 for this welding, after 4 hours, crack was observed on the weld toe,

however there is no crack on the weldment, thus I assume this is cold crack. 

 

Crack was noticed on the railway material, not on SM490A material. 

 

Welding condition:

Baking was done 300-350degC x 1hr 

thickness: 16mm both material 

Preheat: 200degC 

Post heating: 250degC x 1hr

 

Can anyone advise how to solve this crack defects

 

Best regards,

Pravin Poornachandran

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CADDyn7eE6%2Ba9MxkOJQ6oTfKK3xFXmLvXGn0yp5cFjAzWpGt_-A%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CADder3M8d3M7Q1bU0QyJ_%2BS74ftXamPZoCsuYdPM6mjk7vfMWQ%40mail.gmail.com.