Re: [MW:28226] Re: Tensile properties of 6010 and API 5L X70 Pipe

PLS SPECIFY DIA.& THK. OF THE PIPE

Thanks/Regards,

C.R.Bhiwandkar

Supreme Megastructures Pvt. Ltd.

Supreme House, Plot No.-49/C,

Pratap Gad, Opp.-IIT Main Gate.

Powai, Mumbai - 400076

Cell No.:-+919867139337

On Sun, Aug 26, 2018 at 4:36 PM Mohd Siraj <mohd52100@gmail.com> wrote:

asif,

6010+9010 (or 9018 up hill)would be good choice,

8010 would may lead to hot cracking...

On Thursday, August 9, 2018 at 2:48:37 PM UTC+3, Asif Shahzad wrote:

 

Dear Expert,

we need to weld the API 5L X70 grade pipe and using the  electrode 6010 for root, While tensile strength  of the 6010 electrode is 430 MPa while tensile strength of X70 grade is (570 to 760)MPa. So tensile strength of 6010 is lower than x70.For hot pass, filling and capping we are using 9010.

Please provide your expert opinion that we can use the electrode having low tensile strength than the base metal  and if yes kindly give the reason

Regards,

Asif

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.