Dear Harish.

Thank you for responding.

"The intent is to test a specimen representing as nearly as possible the material as used in service. The specimens should be cut to represent the grain flow direction that will see service, for example, specimens should not contain cross-sectional areas unless it is the intent of the test to evaluate these. Only such surface finishing should be performed as is required to remove foreign material and obtain a standard, uniform finish as specified in 6.4. For very heavy sections, specimens should be maintained to represent the appropriate surface while maintaining reasonable specimen size for convenience in testing. Ordinarily, removal of more material than necessary will have little influence on the test results." this paragraph is taken from G28 and only said about the surface area but didn't talk about any thing about cross section or through thickness orientation of sample especially for weld deposited over laid that have a metallurgical & diluted interface can rise possibility of detrimental phase.

Do you have any experience or document that address this issue?

Regards.   

On Wed, Aug 29, 2018 at 11:27 AM Harish Kannepalli <harishkannepalli@gmail.com> wrote:

Hi,

     The sample preparation for clad materials is always debatable and should mostly be addressed by end user specification. It should be dictated from the fact that service fluid is in touch with the final clad layer and considering the corrosion allowance. However you may check the entire cross section corrosion rates for your reference.

Thanks & Regards,
Harish

On Aug 29, 2018 12:10 PM, "Ali Asghari" <asgharialigl@gmail.com> wrote:

Dear All.

Does anybody have any experiences or instruction for preparation of sample for G28?is there any requirement to remove clad material from surface and go through it or not?

this question arises from this point that IGC comes from carbide & inter metallics that mostly possible in diluted area and also accepted corrosion rate is about 0.9 mm/year for 625. Now is it reasonable to prepare sample from interface or without removing of thickness and take it from surface?

Regards.  

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to a topic in the Google Groups "Materials & Welding" group.
To unsubscribe from this topic, visit https://groups.google.com/d/topic/materials-welding/lBI4bYhNtZQ/unsubscribe.
To unsubscribe from this group and all its topics, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.