--Thank you but I have machine shop to machine back to OEM and also a Schenck 6400# balancing machine to balance. My issue is the welding process needed for this material.
What would be your COLD suggestion?
Respectfully,
Butch26
From: materials-welding@googlegroups.com <materials-welding@googlegroups.com> On Behalf Of Nachhattar Singh
Sent: Wednesday, May 02, 2018 10:25 AM
To: materials-welding@googlegroups.com
Subject: Re: [MW:27770] Cracked Impeller Wear Rings
Dear
The impeller rings not to be welded if there are more cracks, because you can't get surface perfection then you will experience the imbalance and the impeller will further get damaged and ultimately purpose will not be solved.
Yes, only one option if you want to go for cold repairs in case of emergency and nonavailability of the resources for building up.
Good luck.
N.S.
On Wed, May 2, 2018, 8:46 PM Butch26 <butchmurrell26@gmail.com> wrote:
Dear experts,
Have several cracks on the wear rings of a Goulds pump Impeller. PMI has been performed and rings have been identified as --17-4 Ph. The impeller itself is a mild c/s.
Have no references on welding these two metals together? Any ideas or procedures?
Respectfully,
Butch26
--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
Visit this group at https://groups.google.com/group/materials-welding.
For more options, visit https://groups.google.com/d/optout.
No comments:
Post a Comment