Dear Mr. Arslan,
For this kind of casting material we always use the following filler metal, it's a GMAW wire. I'm sure you also can use this one for your application as well or you can look at your local supplier for a filler metal with similar code. If you choose another welding process you should also look in this direction.
G CrMo 1 Si / ER 80S-G / Union I CrMo / Böhler Thyssen |
Met vriendelijke groeten / Best Regards
Herman Pieper
Pieper Quality Support & Inspection
Phone: +31 (0)521 380083
Fax: +31 (0)84 7539225
Cell: +31 (0)6 51691215
www.pieper-qsi.nl
Van: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] Namens Sinan ARSLAN
Verzonden: donderdag 11 augustus 2011 7:27
Aan: materials-welding@googlegroups.com
Onderwerp: [MW:12181] 42CrMo4 ( SAE 4140 ) Welding
Hi,
As you seen on drawing we will do fillet weld at this ring.The material grade 42CrMo4 ( SAE 4140 ).
I searched on internet it must be apply preheating which degree nearly 316ᵒ C before welding and after welding it must be apply heat thearetment ( 590 ᵒC-600 ᵒC ) and than cool down at room temperature.
Now i am looking an electrode for this material.
At enclosed i added speciality for this material.Could you advice me an electrode for this material?Which electrode?
--
Saygılarımla.
Best Regards.
Sinan ARSLAN
Mechanical Eng.
Welding Eng.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment