hi, As it has a poor weld profile if should be rejected. Regards
--- On Fri, 26/8/11, sedef pala <santasatana@gmail.com> wrote:
From: sedef pala <santasatana@gmail.com>
Subject: [MW:12313] change in welding color in Cr Mo V steel
To: "materials-welding" <materials-welding@googlegroups.com>
Date: Friday, 26 August, 2011, 11:13 PM
Hi to Everybody, Attached i included two photos from welding (material Cr Mo V steel, process TIG ). As you can see from picture there is change in color of the weld.Visualy my interpretation is that welder increaed welding speed (therefore heat input was decreased), in copper colored area he welded more faster and made weld puddles more thick.Where on left side color of the weld pool looks good(similar to base material) and paddles are in range. My question is " if the weld puddles looks thicker and color is like copper can it be rejected, especially in welders skill test"? Thanks in advance for any opinion. -- To post to this group, send email to materials-welding@googlegroups.com To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com For more options, visit this group's bolg at http://materials-welding.blogspot.com/The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
|
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at
http://materials-welding.blogspot.com/ The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment