[MW:3649] Re: Regarding PQR/WPS

By Materials & Welding
Dear All,
 
I have one PQR for SMAW process and welding electrodes used for qualification are E6010 (root) and E6013 (for sebsequent passes). Anybody can advise me whether I can develop a WPS from this PQR with E6013 welding electrode for both root and other passes.
 
Regards
 
Santhosh

--- On Fri, 11/13/09, Pablo Acelajado <pjacelajado@npc.com.sa> wrote:

From: Pablo Acelajado <pjacelajado@npc.com.sa>
Subject: [MW:3648] RE: 3639] Re: Criteria of HIC testing CSR, CTR and CLR ratio.
To: materials-welding@googlegroups.com
Date: Friday, November 13, 2009, 3:46 PM

 

November 13, 2009

 

Please use NACE TM0284:2003. Thanks.

Pablo

SAVE TREES  - THINK BEFORE YOU PRINT

From: materials-welding@googlegroups.com [mailto: materials-welding@googlegroups.com ] On Behalf Of Ramprasad Chari
Sent: Thursday, November 12, 2009 7:31 AM
To: materials-welding@googlegroups.com
Subject: [MW:3639] Re: Criteria of HIC testing CSR, CTR and CLR ratio.

 

In my opinion,client needs to specify "crack resistance service" desired by them.Like SOHIC & SZC are to be done for some severe conditions especially applicable for Plates.HIC resistance is more critical and calls for a controlled chemistry of elements especially Sulphur level.Severity is decoded by partial pressure of H2S and its mole fraction.Again as per my understanding "generalized" compliance to NACE std may not be correct.

If you refer page 41(Annexe E) of the std,it calls for confirmation by Material Purchase i.e.Customer.

Hope I have made myself clear.

Regards

Aarpee

On Thu, Nov 12, 2009 at 8:23 AM, Bagesh Kumar <bagesh.kmr@gmail.com> wrote:

Dear All,

         I have gone through the Nace MR 0175/ISO 15156, the HIC and SCC has to be carried out on the materials according to the standard.

Now I have gone through a project specification in which the client has specified clearly the requirement of HIC Testing, SSC testing on Pipes, Fittings, and Valves separately apart from the above stated standard requirement.

Another Project specification of different client do not specify these testing separately but they desire the materials to be according to NACE MR 0175/15156,

My question remains: Is HIC and SSC testing mandatory on all piping components for SOUR Services? if yes then please get me the code reference for it.

And also illustrate the CSR (Crack sensitive ratio) other two results like CLR and CSR.

The discussion on the chapter shall be appreciated.

Thanking You.

Bagesh.

 

 





--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

Comments

Post a Comment

Popular posts from this blog

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

[MW:36169] Cold Bending Qualification

By Materials & Welding
Dear Experts,  Can anyone share the inspection requirements or a qualification procedure for cold bending? Our client spec states only the requirements for induction bending and would like to know your opinion on the cold bend inspection requirements. The code of construction is B31.3, Max. 5D bends, A106 SS 316L.  Thanks in Advance. -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion visit https://groups.google.com/d/msgid/materials-welding/1be61cc3-e9c9-4a5f-834d-e8485e248432n%40googlegroups.com .
Post a Comment
Read more

[MW:30043] Weep hole

By Materials & Welding
If weep hole is not provided in dummy pipe before welding What will happen??? -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/da251ee6-fa7f-4851-b876-cdb3834ae341%40googlegroups.com .