[MW:22197] Bending of Al 5083 plate

Dear Experts,
 
I need your expert advice on following:
 
We are working with Aluminium Al 5083 H-112 grade material. Presently, while doing cold bending/rolling of 57 mm plate of it to make it into cylinder we are experiencing that the OD/ID is not achieving as per reqiurements. Can we do the correction it in this case by flame heating as we generally do with the similar jobs of Mild steel.
If it is, then what should be the heating temerature and the duration of heating?
If there is any alternative method to repair/manufacture it using cold working?
 
Best Regards
Sushant Thakur

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

No comments:

[MW:35346] Cast-iron welding

Any advice for cast iron welding Sent from Yahoo Mail for iPhone