Dear Experts,

We are facing the problem bend test failure for Aluminum TIG welding. Its failing for HAZ and getting crack for transverse face bend, Root bend sample (10 mm thickness as welded sample). Pls give some details to bend for aluminum sample, If anyone have experience in aluminum TIG welding. Pls share your experience and provide some welding guideline. What could be the reason of failure or the bend testing requirement for Aluminum welding.

 

Process:           GTAW

Filler:                ER5183

Base Material:   ASME SB209 Grade 5083-O

Code:               ASME IX

Thickness:        10 mm

 

Thanks & Regards,

Mohd. Azam

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/d/optout.