Re: [MW:31861] PWHT required after Preheat for CS or LTCS

In order to reduce the risk of cold cracks due to thickness and stress, PWHT can be applied to provide slow cooling after welding.

Jamie Reyes <jamiejrmachineco@gmail.com>, 17 Ara 2020 Per, 06:55 tarihinde şunu yazdı:
What is the code of construction?
What is the type of service?
Is Lethal Services involved?
Need the above mentioned information.....

Regards,
Jamie Reyes
J.R. Machine Company, Inc.


On Wed, Dec 16, 2020 at 7:47 PM thanh tung Nguyen <tungexp.268@gmail.com> wrote:
Dear Experts,

Hope you all are well.

I have a question is about the weld of the base material of CS (or Low temp. CS) with wall thickness greater than 25mm, Do we still required PWHT if we applied a preheating process before, or PWHT is no longer mandatory?

And which reference can be found?

Thank you & best regards./.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAKr%2BxwbEWDaz5Lo9eQpu_iY7m4Gewk3V9A%3D556vTj9QwUkBHQQ%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJNUtUPCr_fxg1Ep1iYS-ozi5XG1vBHajiJ_Sf06paBaW9R97g%40mail.gmail.com.


--

Regards / Saygılarımla

 

Furkan TOPALOĞLU

Metallurgy and Material & Welding Engineer

Metalurji ve Malzeme & Kaynak Mühendisi

Phone : +90 (539) 437 88 03

E-Mail : topaloglufurkan8@gmail.com

 

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CALZR%3D4SC_A6X9qw-8Xvf5Gpw6YVgy1MnN9QpVBegJLNurqrxuQ%40mail.gmail.com.

No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...