When plate is bonded by explosion. The shape of the plate is disturbed, resulting in stresses and higher hardness. In order to straighten it up, it is always recommended to do a stress relieving heat treatment. It is nowhere specified, but to avoid issues during straightening and control hardness.
On Thu, 3 Dec 2020 at 15:37 udaya bhaskar <dusroni@gmail.com> wrote:
Mr.Patel, Doesn't require any PWHT after explosive cladding.if the customer wants you can, otherwise not.On Thu, Dec 3, 2020 at 8:34 AM Patel Ankit <aapatel271@gmail.com> wrote:Yes sir,After Bonding PWHT required or not??--On Thu 3 Dec, 2020, 9:00 AM George Dilintas, <dilintas@gmail.com> wrote:What do you mean by bondingΣτις Τετ, 2 Δεκ 2020 στις 5:12 π.μ., ο/η Patel Ankit <aapatel271@gmail.com> έγραψε:Dear Expert,--I hope all are well.My question is In after Tubesheet Bonding PWHT required or Not?Base Material : SA 516 GR 70. (Thk : 45 mm )Bonding Material : SA 240 GR 316. (Thk:5mm)Tubesheet Dia : 3000 mm( Note : Bonding plate SS 316 : 1 No joint on base material)Regards,Ankit Patel8140255303.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CALR-PuwRp0-NoHz6KXB6-4Y3tkTKmaB4pJxtF8HhM8ctpf3EtA%40mail.gmail.com.
----Dr. Georgios Dilintas,Dipl. Ing. In Aeronautic and Space EngineeringPh.D in Mechanics of Solids - Computational MechanicsA.I.S, A.N.I, IRCA Lead AuditorWelding, Stress Analysis, Corrosion, QA/QC, Failure Analysis, Risk Analysis
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAPOi40CjGONDt6HonTPf4vP1h_MmXkyu76RSLh7pykTRw10Uig%40mail.gmail.com.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CALR-PuyDQdbY3rMmc%2BFcZVTP%2BvFyX4r5MJt5Lnkhjw7kbA7x_Q%40mail.gmail.com.
----With RegardsUdaya bahaskar.D+919676270121
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CANii3RNRi9qNctSjHmBcOy07SeeJd%3DohSRNQMoOqWUPb0bSAuA%40mail.gmail.com.
Regards,
Nithin Joseph Dsilva
Nithin Joseph Dsilva
+971 557645785
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAFS9gDP9ZvPzC8ABGR1u7v4O61kPc3pyOgtxjG_DBdkcS9tD6w%40mail.gmail.com.
No comments:
Post a Comment