This is due to joint design, deeper / narrow the joint difficult to remove slag
On Mon, 16 Dec 2019 8:39 am Dharma dattu, <dharmadattu@gmail.com> wrote:
Hello All,--We have a job with 30 degree single bevel corner joint, as per client requirement we are using SAW process to complete on time schedule.the fact is for root run the slag is not easy to be removed, as its hard and taking a lot of time even for grinding wheel / chipping. can some one say the reason for it. or a solution.Subsequent layers slag is releasing on it's own, so i don't doubt filler metal or flux.we are at present using base metal 20mm thk and 4mm filler metal, brand, D&H.Regards,Dharma Dattu. B
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/ff2af474-4f1c-48e0-8ee6-e284a0228a4e%40googlegroups.com.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJzm4eOeyUyHWmhxNjJ2vXdtgiG%3DwR7f2%3D%2BCtou5yVta_rs8-Q%40mail.gmail.com.
No comments:
Post a Comment