[MW:3083] Re: Regarding the NDT to be carried out for 60 mm thick austenitic stainless steel plates

By Materials & Welding
Nilesh,
Why would you do these things?
1. No co60 for 69 mm SS?
2. High Strength and Low Strength Ir 192 are same in their pen power.
3. UT of 60 mm SS - well, can you please pass me the proc? I am curious. Twin crystal for what reasons?
Shashank Vagal

--- On Sun, 30/8/09, SENTHILKUMAR SWAMINATHAN <skumarswami@yahoo.co.in> wrote:

From: SENTHILKUMAR SWAMINATHAN <skumarswami@yahoo.co.in>
Subject: [MW:3082] Re: Regarding the NDT to be carried out for 60 mm thick austenitic stainless steel plates
To: materials-welding@googlegroups.com
Date: Sunday, 30 August, 2009, 2:44 PM

High Curie or Low Curie only helps in time factor. But Ir 192 Penetration is same from Low and High. If am wrong correct me.
 
S.Senthilkumar

--- On Sun, 30/8/09, Yadav Shiva <luvshiv2002@gmail.com> wrote:

From: Yadav Shiva <luvshiv2002@gmail.com>
Subject: [MW:3080] Re: Regarding the NDT to be carried out for 60 mm thick austenitic stainless steel plates
To: materials-welding@googlegroups.com
Date: Sunday, 30 August, 2009, 2:38 PM

hi,
           you can go for high strength - 192, but dont go for cobalt 60 since we use for thickness ranging more than 100 to  & 150 mm above.

On Sun, Aug 30, 2009 at 11:48 AM, Nilesh Pathare <patharenil@gmail.com> wrote:
Hi,
If your specification permits for RT or UT you can carry out any of these test for 60 mm Thick S.S.
For RT you may need cobalt 60 or High strength iridium 192.
For Ultrasonic Testing you shall use the RTD Twin crystal longitudinal wave Angle probes.

Regards,
Nilesh Pathare.

On Sun, Aug 30, 2009 at 10:35 AM, Stephen <stephenipr@gmail.com> wrote:

I wanted to know which NDT to be carried out for 60 mm thick
austenitic stainless steel plates welded using TIG welding





--
Best Regards,

Nilesh Pathare




start: 2008-06-21 end: 0000-00-00
Looking for local information? Find it on Yahoo! Local


See the Web's breaking stories, chosen by people like you. Check out Yahoo! Buzz
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

Comments

Post a Comment

Popular posts from this blog

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Re: [MW:10788] ON PLOT PIPING & OFF PLOT PIPING

By Materials & Welding
Piping systems involved for the flow lines and gathering lines from the well head isolation valve to the production facility or processing plant isolation valve are determined as OFF PLOT. ON PLOT defines piping system in the processing plant and production platform. ANSI/ASME B31.4 applies for off plot piping system. B31.4 allows the use of either API 1104 or ASME section IX (as appropriate). However, occasionally, a very small system such as piping within 500 feet of a processing plant (some client also said 400 feet) may be declared B31.3 rather than B31.4. When B31.3 is invoked, only ASME Section IX is used. before you decide which code to use for welding procedure and/or welder qualification for pipe welding, you have to know the design and construction code applicable to the system. Please read far enough into scope and diagram illustrating the application of either B31.3 and B31.4 hope this helps rgds 2011/4/21 pradip kumar sil < pradipsil@gmail.com > Dear all, ...
Post a Comment
Read more