Yes, performing furnace PWHT on any joint that was welded using a WPS not qualified with PWHT violates Clause 331.1.6(b) of ASME B31.3. It constitutes a quality non-conformance, even if the individual weld is below the threshold thickness for mandatory PWHT.
BR,
Deerendra
As per ASME B31.3, Clause 331.1.6 (b):
Any required PWHT shall be carried out in accordance with the qualified WPS.For furnace PWHT involving spools of different diameters and varying thicknesses, all weld joints subjected to PWHT must be welded using a WPS qualified with PWHT. This requirement remains applicable even when the individual joint thickness is less than 20 mm, despite the code-specified threshold of greater than 20 mm for P1 materials, as outlined in Table 331.1.1 of ASME B31.3 (2008).
Therefore, performing furnace PWHT on any joint that was welded using a WPS not approved for PWHT constitutes a non-conformance with the applicable quality requirements. Do you agree? If not please elaborate.
Prakash
--On Sat, Apr 5, 2025 at 7:52 AM Hareesh K V <hareesh.kitco@gmail.com> wrote:Dear Sir,I am not clear about the question.Is the question is "The welding is done without following a WPS having PWHT and actually the joints need the same" is it?May I know the material ?Also if it is of Carbon Steel material, is PWHT requirment is there based on design or based on ASME 31.3?Regards,Hareesh K V--On Mon, 27 Jan, 2025, 11:57 am Prakash Kumar Bontra, <prakashbontra@gmail.com> wrote:For furnace PWHT as per ASME B 31.3 all the joints in the spool (1" to 36") need PWHT approved WPS and where to refer?--Prakash Bontra
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CANeLWoNy0URXS9X7TEvvZRVe4V-1LNPKwidHJ097fDyPAjyh7Q%40mail.gmail.com.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to a topic in the Google Groups "Materials & Welding" group.
To unsubscribe from this topic, visit https://groups.google.com/d/topic/materials-welding/oPoxrZeCuSA/unsubscribe.
To unsubscribe from this group and all its topics, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CAEv1fk_qTuLX3BbXwWEmjZYkHEKJg5fYEQ4n3tV28CtXxXG8DA%40mail.gmail.com.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CANeLWoNcLHBndkp%3DRS5noKQnJLek4y7Ku9xuQHgAK7-WcZJ%2B4A%40mail.gmail.com.
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CAG0nF9HGKViUYO-Uj_uXgPb3e4fVkX7ZKeMTkbUD9t8XZ9osBw%40mail.gmail.com.
Comments