RE: [MW:31006] Filler rod selection for SS 304L to SA 335 pipe welding

E/ER-312, with a high ferrite content, will also experience severe embrittlement at elevated temperatures. 

 

From: 'wilfred kojo' via Materials & Welding [mailto:materials-welding@googlegroups.com]
Sent: Sunday, June 14, 2020 11:00 PM
To: materials-welding@googlegroups.com
Subject: Re: [MW:31005] Filler rod selection for SS 304L to SA 335 pipe welding

 

Hi,

For high temperature service, ER312 or E312 is not a good choice due to difference in coefficient of thermal expansion between 312 and ferritic steel which cause early failure.

 

On Monday, 15 June 2020, 04:39:14 GMT+1, harenath jha <harenathjha@gmail.com> wrote:

 

 

Basis of selection please ?

 

On Sun, Jun 14, 2020, 21:39 Chintan <chintan51@gmail.com> wrote:

Use ER312 & E312

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/b498dd65-4ebe-4eca-827a-7db9e5f691a5o%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAPRS9UOr8MuMLc_AW3a6tKqZBJsc_O6XYbz4i6vDHLC5AD-kow%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/927274983.1200664.1592193618866%40mail.yahoo.com.

DISCLAIMER This e-mail and any attachments thereto may contain information which is confidential and/or protected by intellectual property rights and are intended for the sole use of the recipient(s)named above. Any use of the information contained herein (including, but not limited to, total or partial reproduction, communication or distribution in any form) by persons other than the designated recipient(s) is prohibited. If you have received this e-mail in error, please notify the sender either by telephone or by e-mail and delete the material from any computer.
General Data Protection Regulation (GDPR)
We respect and protect your privacy to provide you with our services. Please read https://www.hamon.com/customer-data-protection-notice (Customer) and https://www.hamon.com/seller-data-protection-notice (Supplier) how we process your personal data.

Thank you for your cooperation.
______________________________________________________________________

No comments:

Re: [MW:35241] Overlay welding defects

Dear Sir, The below is another type of defect,Mostly these two type of defects we faced. Regards, R.Gowtham. On Wed, Sep 11, 2024 at 1:42 PM...