On 6/4/13, Chan, David <David.Chan@exterran.com> wrote:
> Hi Michael,
> If the deposited weld metal of GTAW is 5.0mm and SMAW 14.0mm respectively
> (making it a total of 19.0mm in weldment) , then there is a high possibility
> of incorrect reporting where the test specimen of 10.31 mm could not have a
> total weld deposit of 19mm. It seems to be incorrectly reported
>
> It is very likely to be welded as 2.5mm and 7.31mm for the weld process of
> GTW and SMAW respectively which will gives you a qualified thickness of
> 5.0mm for GTAW and 14.6 mm for SMAW process
>
> Maybe, you could like to check the PQR one more time
>
> Thank you
> Best Regards
>
> David Chan
> Singapore
>
> From:
> materials-welding@googlegroups.com<mailto:materials-welding@googlegroups.com>
> [mailto:materials-welding@googlegroups.com] On Behalf Of Michael Lawrence
> Arokiasamy
> Sent: Sunday, June 02, 2013 1:49 PM
> To:
> materials-welding@googlegroups.com<mailto:materials-welding@googlegroups.com>
> Subject: [MW:17866] Deposited weld metals
>
> Dear All,
> Please clarify my doubt in WPS as per ASME SECTION IX
> Process: GTAW + SMAW
> PQR base metal Thickness: 10.31 mm
> WPS Base metal thickness range: 5.0-19.0 mm
> Deposited weld metal: GTAW (5mm)+ SMAW (14mm)
> How I can find out the weld metal thickness GTAW 5mm & SMAW 20.62mm
> (I saw the section IX, QW-404.30 & QW-450 Table also but I can't
> understand)
>
> Thank you,
>
> Regards,
> A.Michael Lawrence
> Welding Inspector
> 0060 105111044.
> --
> To post to this group, send email to
> materials-welding@googlegroups.com<mailto:materials-welding@googlegroups.com>
> To unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.com<mailto:materials-welding+unsubscribe@googlegroups.com>
> For more options, visit this group's bolg at
> http://materials-welding.blogspot.com/
> http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
>
> The views expressed/exchnaged in this group are members personel views and
> meant for educational purposes only, Users must take their own decisions
> w.r.t. applicable code/standard/contract documents.
> ---
> You received this message because you are subscribed to the Google Groups
> "Materials & Welding" group.
> To unsubscribe from this group and stop receiving emails from it, send an
> email to
> materials-welding+unsubscribe@googlegroups.com<mailto:materials-welding+unsubscribe@googlegroups.com>.
> For more options, visit https://groups.google.com/groups/opt_out.
>
>
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.com
> For more options, visit this group's bolg at
> http://materials-welding.blogspot.com/
> http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
>
> The views expressed/exchnaged in this group are members personel views and
> meant for educational purposes only, Users must take their own decisions
> w.r.t. applicable code/standard/contract documents.
> ---
> You received this message because you are subscribed to the Google Groups
> "Materials & Welding" group.
> To unsubscribe from this group and stop receiving emails from it, send an
> email to materials-welding+unsubscribe@googlegroups.com.
> For more options, visit https://groups.google.com/groups/opt_out.
>
>
>
--
*Ramin Kondori*
*Sr. QA/QC Engineer
*
*SINOPEC*
r.kondori@petroyada.com
+98-2123592322
+98-9132150320
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.
Subscribe to:
Post Comments (Atom)
Re: [MW:35686] HDPE WPS
Refer ASME SEC IX There is separate chapter for Plastic welding . Based on that you have to prepare Sent from my iPhone On 21 Jun 2025, at...
-
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
-
Definition of buttering from ASME Section IX, QW/QB-492 Definitions: Buttering: the addition of material, by welding, on one or bot...
-
Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...
No comments:
Post a Comment