Re: [MW:10515] SS 304 WIRE WELDING

Do you mean that the distortion after welding shall be within +/-0.15mm? If its so then preferable solution would be Flash butt welding as the one used for welding coils in the electrode manufacturing. This technique provides a faster and efficient solution with little compromise on microstructure.


 
On Sun, Mar 27, 2011 at 4:19 PM, <compmg@rediffmail.com> wrote:
Dear Friends,

We are looking for the solution to weld 3 mm SS 304 wire.  the tolerances are as follows

Weld Point Material formation and demormation +/- 0.15 mm

Could you please provide us the best solution to control this in production.

We have the daily production target of 100000 pcs.

Warm Regards,

KUNAL KHATRI

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...