hi 

WPS is 2001 and after your  material BS EN 10025 is also revised check it with latest then compare any changes in base metal. Other thing is if Third party is not approving it or your client is not approving then you have to qualify fresh PQR.

2. yes.

On Sun, 27 Mar 2011 20:15:09 , manoj john <manojacgnr@gmail.com> wrote
Dear members,

I have one query regarding WPS.

1) One of my client made a comment on a WPS which i had submitted to
them for approvel that  Procedures are from 2001.  My question is Is
there any time limit for WPS?  In my knowledge answer is No, a
qulified procedure can be used any time without changing the essential
variable.

2) I have one  qualified wps with base metal S 355 JR to S 275 JR.
Can I use this WPS to weld  S 355 JR to S 355 JR and S 275 JR to S 275
JR?

Please clear my doubts, if possible with code reference.

Thanks & Regards.

Manoj

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...