Re: [MW:33594] HEAT EXCHANGER CONSTRUCTION

By Materials & Welding
Thanks 
Pl help to inform the  name of the book /literature from where the below  snap  is taken

Thanks and regards

Vishwas 



On Tuesday, October 11, 2022 at 11:19:23 AM UTC+5:30 gerry_tup wrote:
Just some info on 475degC embrittlement.

Inline image
Inline image
Inline image
Inline image


Thanks & Regards

J.Gerald Jayakumar


On Tuesday, 11 October, 2022 at 07:24:35 am GMT+4, 'james gerald' via Materials & Welding <material...@googlegroups.com> wrote:


sorry for being out of track.

I believe the welding between Tube sheet and Shell/Channel via a LIP provided in the TS forging where you can excercise a control.

Ensure DSS is not exposed to temperature greater than 400 degC to avoid 475 embrittlement (alpha prime intermetallic)

Thanks & Regards

J.Gerald Jayakumar



On Monday, 10 October, 2022 at 12:55:58 pm GMT+4, Vishwas Keskar Welding Manager WELDING <vvkes...@gmail.com> wrote:


Pl. note that all the HEX Tubes are also of DSS TYP S32205 .
  So  the concerned is for these DSS tubes also.

On Monday, October 10, 2022 at 11:38:58 AM UTC+5:30 gerry_tup wrote:
Thanks Prabhu.

Is SCC in chloride environment  a problem with SASS & 625.

Moreover SASS are available mostly in European market.

Thanks & Regards

J.Gerald Jayakumar


On Monday, 10 October, 2022 at 09:37:06 am GMT+4, 'Prabhu kumar Loganathan' via Materials & Welding <material...@googlegroups.com> wrote:


Hello Gerald,

Yes, below specified Super ASS is an alternate to DSS due to high Cl environment, however market availability is very less which leads to long delivery time and hence suggested to go for Inconel 825 or 625, again Alloy 825 weld deposition is having cracking issues >5mm thick which is not recommended.

Regards,
L. Prabhu kumar



From: "\'james gerald\' via Materials & Welding" <material...@googlegroups.com>
Sent: Mon, 10 Oct 2022 08:55:39
To: 'Prabhu kumar Loganathan' via Materials & Welding <material...@googlegroups.com>
Subject: Re: [MW:33563] HEAT EXCHANGER CONSTRUCTION
 
Nice to see you back Prabhu.
 
If service restrictions are only due to chloride concentration then we try the SASS like 904L, 254 SMO & 654 SMO/
 
Your views
 

Thanks & Regards

J.Gerald Jayakumar

 

 
 
On Friday, 7 October, 2022 at 07:33:25 am GMT+4, 'Prabhu kumar Loganathan' via Materials & Welding <material...@googlegroups.com> wrote:
 
 
Hi,
In general, DSS weld overlay is not recommended in CS due to cracking and other weldability issues. Moreover, Tube sheet forging with heavy weld overlay requires stress relieving too. 
However, stress relieving is not recommended for DSS, Hence in my opinion DSS weld overlay on TS to be replaced with Alloy 625 weld overlay wherein all these these issues related to weldability & PWHT will be solved.
Regards,
Prabhu.





From: Vishwas Keskar Welding Manager WELDING <vvkes...@gmail.com>
Sent: Thu, 06 Oct 2022 09:52:15
To: Materials & Welding <material...@googlegroups.com>
Subject: [MW:33541] HEAT EXCHANGER CONSTRUCTION

Dear Experts 
One of HEX involves  following MOCs -
HEX tubes - SA 789 TYP 32205 
Tubesheet -SA 266 CL 2 CS - Tube sheet IS cladded with TYP S32205  overlay.
Shell side - CS -SA 516 GR 70 - 75mm thk 
Channel side - CS- SA 516 GR 70 - 75 mm thk 
PWHT is required for  Tube sheet to Shell welding and Tube sheet to Channel welding. These are butt welds with CS Weld metal .
PWHT is not required for  Tube sheet to HEX Tube  welding due to DSS tube to DSS cladding.
 
Pl advice for the  care that shall be taken during PWHT  of Tube sheet to Shell welding and Tube sheet to Channel welding.
 
Thanks and regards
Vishwas - IWE
International Welding Engineer
 
 

 

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/a163c4a4-fe95-4245...@googlegroups.com.
 

 

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit
https://groups.google.com/d/msgid/materials-welding/1665030135.S.10013.29756.f...@webmail.rediffmail.com
.

 

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/1533605827.35179...@mail.yahoo.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/6a3b7d65-5836-4f67-abfa-b24b6e88551an%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/da57bdef-0903-4496-823b-dbed31173e06n%40googlegroups.com.

Comments

Post a Comment

Popular posts from this blog

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

Re: [MW:10788] ON PLOT PIPING & OFF PLOT PIPING

By Materials & Welding
Piping systems involved for the flow lines and gathering lines from the well head isolation valve to the production facility or processing plant isolation valve are determined as OFF PLOT. ON PLOT defines piping system in the processing plant and production platform. ANSI/ASME B31.4 applies for off plot piping system. B31.4 allows the use of either API 1104 or ASME section IX (as appropriate). However, occasionally, a very small system such as piping within 500 feet of a processing plant (some client also said 400 feet) may be declared B31.3 rather than B31.4. When B31.3 is invoked, only ASME Section IX is used. before you decide which code to use for welding procedure and/or welder qualification for pipe welding, you have to know the design and construction code applicable to the system. Please read far enough into scope and diagram illustrating the application of either B31.3 and B31.4 hope this helps rgds 2011/4/21 pradip kumar sil < pradipsil@gmail.com > Dear all, ...
Post a Comment
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more