Re: [MW:29920] Difference between Control thickness & nominal material thickness ( Para. 331.1.3(c)

Both are used in different occasions

On Sat, 3 Aug 2019 10:36 am anhtrangnghieng, <anhtrangnghieng@gmail.com> wrote:

Dear Experts, 

Could you please advise me for following question: 

Which thickness , Control thickness or Nominal material thicness as defined in Para. 331.1.3(c), shall be used to determine whether PWHT required or not in case preheat of 95 Deg C is NOT applied ? ( P-No. 1)

For case below, in accordance with ASME B31.3 2016 Ed , PWHT is required or not when preheat of 95 Deg C is NOT applied ? 

Thanks in advance.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CADOyxJhXTaZ-607uvbSyYFt-Yqhr-L4%2BoMNyD_dWx8Rax-LRbg%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJzm4eP5UheGb1m9-g%3D6DexLQrRswVmVtbfK5iDrvki7A%3DTsYA%40mail.gmail.com.