Re: [MW:26216] CRA Clad pipeline welding

Re: [MW:26216] CRA Clad pipeline welding - SAES-W-019

Hi Neilashkumar

Thanks for the reply.

The application is girth welding of roll bonded & SAWL CRA-clad line pipe, not weld over lay.

It is agreed that API 1104 is normally applicable for cross country pipeline with carbon steel line pipes.

But the gas transmission pipelines are designed to ASME B31.8 which is specifying to use API 1104 for welding, but SAES-W-019 is specifying to use ASME Sec IX. Of course, Client specifications shall take precedence, but the rationale of applying ASME Sec IX is not clear.

Krishna

On Saturday, 18 March 2017 10:51:45 UTC+8, neilash kumar wrote:

Krishna,

Below interpretation is not clear, can you please share more details on CRA overlay that you intend to qualify? So that I can help u to explain in better way.
SAES W 019 for CRA Girth weld
API 1104 for cross country pipeline,

P.NEILASHKUMAR
Sent from my iPad
MOB : 966 551094590
+91 9952110791

On 17-Mar-2017, at 5:13 AM, Krishnnaa26 <krishna....@gmail.com> wrote:

Deal all

Pipeline design code is ASME B31.8 that is specifying to use API 1104 for gas transmission pipelines.

But, SAES-W-019 specifying to use ASME Section IX,

Do anyone received approval to use of API 1104 for CRA-Clad pipeline welding,

Thanking you

Krishna

--
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
To post to this group, send email to material...@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/f6e5fa60-b019-4a36-8502-78cc438021a6%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

--
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/565e64ef-9bc8-4910-a364-fbf5c5cd9e6a%40googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Re: [MW:10788] ON PLOT PIPING & OFF PLOT PIPING

Piping systems involved for the flow lines and gathering lines from the well head isolation valve to the production facility or processing plant isolation valve are determined as OFF PLOT. ON PLOT defines piping system in the processing plant and production platform. ANSI/ASME B31.4 applies for off plot piping system. B31.4 allows the use of either API 1104 or ASME section IX (as appropriate). However, occasionally, a very small system such as piping within 500 feet of a processing plant (some client also said 400 feet) may be declared B31.3 rather than B31.4. When B31.3 is invoked, only ASME Section IX is used. before you decide which code to use for welding procedure and/or welder qualification for pipe welding, you have to know the design and construction code applicable to the system. Please read far enough into scope and diagram illustrating the application of either B31.3 and B31.4 hope this helps rgds 2011/4/21 pradip kumar sil < pradipsil@gmail.com > Dear all, ...

Materials & Welding

Search This Blog