Thanks Hedge,
Buttering shall be with P91 filler? If so, kindly explain the basic technical reason.
S.Binoy
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Prakash Hegde
Sent: Monday, April 08, 2013 12:55 PM
To: materials-welding@googlegroups.com
Subject: Re: [MW:17311] PWHT for P15E to P3
Dear Mr Binoy i) As per ASME code P3 Gr 1,2 does not require PWHT if its thk is less than 16mm and For Gr3 It is manadatory for any thk and temp is min 593 C ii) For P15E (P91) the PWHt is mandatory at 730C Now if the weld joint P15E to P3 undergoesPWHT at 730C temp It will be afftecting the mechanical properties of P3 ( C% 0.5 Mo) Therefore My openion is Better butter the weld edge of P15E with suitable P91 filler and conduct the PWHT of P15E (P91)as per code at 730C and later on weld that edge with P3 (C % 0.5Mo) consumable and that joint need not be PWHT if it is P3 Gr1 or 2 In this case re is no deteoriation of P3 properties However PQR require to be qualified with above condition Regards Hegde
P15E to P15E PWHT cycle that we are following is attached. S.Binoy -- |
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.
No comments:
Post a Comment