[MW:3593] Fw: [MW:3578] WPS/PQR

Dear all,
the PQR can be used without any change but you must make a new revision of your WPS
and the limits will be from 1.5 or 5 mm  to 2T according to the thickness of PQR piece and all suplementary essentioal value will be non essentional

Best Regards ,
ENG. Ahmed Osman

--- On Tue, 11/3/09, tong tong <tong2je@gmail.com> wrote:

From: tong tong <tong2je@gmail.com>
Subject: [MW:3578] WPS/PQR
To: materials-welding@googlegroups.com
Received: Tuesday, November 3, 2009, 12:53 PM

Dear All
I have question regarding WPS/PQR matter. I have one qualified WPS/PQR (GTAW/SMAW) which the base metal spec. is SA 333 Gr. 6 and was impact tested at -50C. Can this PQR support a new WPS to weld SA 106 Gr. B without impact test(not required by code) . What will be the ranges of qualification? is it i need to remove the impact test result on old PQR and allowed by ASME IX code? Please help me. Thank in advance
Regards


Ask a question on any topic and get answers from real people. Go to Yahoo! Answers. --~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

By -

No comments:

Post a Comment

Subscribe to: Post Comments (Atom)

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...

  • Materails FAQs
    Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? ...
  • RE: [MW:5585] Buttering of weld joints
    Definition of buttering from ASME Section IX, QW/QB-492 Definitions:   Buttering:  the addition of material, by welding, on one or bot...
  • WELD AND WELDING SYMBOLS
    Section I. PRINT READING 3-1. GENERAL a. Drawings . Drawing or sketching is a universal language used to convey all necessary information to...