The practice E table 5 specifies that for all grades Ditch structure as non acceptable. step, dual, end grain I and II as acceptable structure.
This is as per A262-02a e3 edition.
With regards,
Kannan Sundaram.
| "Bathula Raghuram \(Mumbai - PIPING\)" <R.Bathula@ticb.com> Sent by: materials-welding@googlegroups.com 29/02/2008 12:27
|
|
ASTM A 262 Practice E does not specify anything about the acceptance of Interdendritic ditch structure (refer Table 5)
Where as in others (like in practice C it is specified in non acceptance category)
When a report specifies for weld IGC as Interdendritic ditch structure, is it acceptable?