Use pulsed TIG.
Ravinder
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of PREM SHANKARDUTT NAUTIYAL
Sent: Monday, May 11, 2009 10:42 PM
To: nchinoy@gmail.com
Cc: materials-welding@googlegroups.com
Subject: [MW:2150] Re: Welding GI Sheets
Hi Nimesh
Are u using any filler wire ?
If yes then,trust you are using ER70S2 which is a good deoxidised wire.
Also i would suggest you grind the area to be welded i.e WEP prior to welding. We have welded GI pipes with same procedure by TIG successfully.
Regards
Prem S Nautiyal
Godrej,Mumbai.
On Mon, 11 May 2009 10:49:13 +0530 wrote
>Dear All,
>
>We are trying to weld Galvanised Sheets 0.5mm with GTAW. We find it
>difficult to weld and get some blow holes. Results with CRC instead of
>galvanised are much better.
>
>Is this because of the Zinc content ? Any suggestions ?
>
>Regards,
>
>--
>Nimesh S Chinoy
>
>>
>
PREM S NAUTIYAL
CELL : 9820313278
|
|
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---
No comments:
Post a Comment