Re: [MW:35735] Bend Test and Tensile Test failed for ET45 Micro Welded Coupon

Hi ,

 We have worked on same material but fillers seems incorrect ,may be you try with UTPA 3545nb.

And bent test you can't proceed similar as normal material as it's having low ductility . 

Best regards 

On Sat, 26 Jul 2025 at 2:04 PM ROHAN SONI <sonirohan94@gmail.com> wrote:

Dear Team, 

I am working on a material called ET45 micro (GX45NiCrSiNb45-35 Material) 

Elongation is 3 to 5℅

Tensile stength -450 Mpa

Consumable- ERNICRMO-3 

Due to such lower Elongation material shows brittle fracture and immediately failed from HAZ. 

During tensile testing it is failed from Where it holds from base metal. 

Kindly provide the solution for this that how can i comply the PQR testing. 

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CAMQ93h8E5kdWag0gJa6tyqzRzG6qg%3D1KZ%2B3d_bBd6sKnOR%2Bjkw%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CAOgMkxHHuhDi_m27tqOArrWa76%3Djs9zUwEBp6M4N56sKgN%2Bb5Q%40mail.gmail.com.