Re: [MW:34882] PWHT of Normalized head

PWHT required specific holding time and controlled cooling as per sec VIII Div.1. Normalizing having air cooling after reaching at 900 deg c.  Since normalizing not required specified holding time and controlled cooling, will it substitute ?

Thanks & Regards
Muhammed Ibrahim PK

On Mon, 15 Apr 2024 at 7:59 PM venkateswara reddy Desireddy <dvreddy82@gmail.com> wrote:

Hi, 

If you heat treated 900°C , then no need to do 610°C. 

On Mon, 15 Apr 2024, 4:05 pm anthony chundal, <anthony.chundal@gmail.com> wrote:

Hi

PWHT is required for 45 thk, normalizing is separate heat treatment and cant be combined with stress relieving,

Regards,

On Sun, Apr 14, 2024 at 4:56 PM Muhammed Ibrahim PK <ibratech@gmail.com> wrote:

Gentlemen,

Is PWHT can be avoided if the welded head (2 piece construction) performs normalizing after forming ?

Head MOC : SA516 Gr 70, 45 mm thk, fabricated by welding the blank in two pieces. 

Complete vessel not required PWHT.

Thanks & Regards

Muhammed Ibrahim PK

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CALOPgmMorLP3zvhePLHgVGFbcpx-t-%2BSd3M6EQpsfpHrAs38Ow%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAOi%3DZp_yfMnLqJsy9WdQhYq%2B24k2an4dznaaYgJH-GHGRbWcDw%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAEabyKk7%2BZva7ZY1EZmHWHXELJ04%2BDprqb_tkQ%2BKmQ9YG-Kb1Q%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CALOPgmPgeetjjqP%3DTEzbgG%3D%3D0msoNX5yEXMJC3uWAPB5Xhd5sg%40mail.gmail.com.