Re: [MW:34917] Applicability of Impact requirement as per ASME B31.3

Dear Vinit,

For the applicability of PQR impact requirements based on the provided details, we need to refer to the ASME Boiler and Pressure Vessel Code (BPVC) Section IX, which covers welding qualifications.

Since you're dealing with welding and materials in the context of ASME BPVC Section IX, the specific clause relevant to your scenario would be Clause QW-402.2. This clause outlines the impact test requirements for procedure qualification.

Based on the information provided:

Material: SA 333Gr6 (P No.1 Gr. 1) to SA 350-LF2 (P No.1 Gr. 2)
Thickness range: 5.54mm (Minimum) - 9.53mm (Maximum)
PWHT: Nil
MDMT: -45 Deg Cel.

Given these details, you would need to assess if impact testing is required for the welding procedure qualification. The decision would depend on factors such as the material specification, thickness, service conditions, and design requirements.

According to ASME BPVC Section IX, if the design temperature is equal to or colder than the Minimum Design Metal Temperature (MDMT) of the material, impact testing may be required. In your case, the MDMT is -45 Deg Cel., and since the design temperature is not mentioned, it's essential to evaluate whether it's equal to or colder than -45 Deg Cel.

Furthermore, Clause QW-403.6 provides exemptions from impact testing for certain materials, thicknesses, and service conditions. It's crucial to review this clause to see if any exemptions apply to your specific scenario.

Ultimately, the applicability of PQR impact requirements would depend on a detailed assessment of the specific welding procedure, material properties, thicknesses, and design conditions, in accordance with the ASME BPVC Section IX.

Regards,

Amol K.Betkar

On Wed, 24 Apr 2024 at 18:59, 'vinit vani' via Materials & Welding <materials-welding@googlegroups.com> wrote:

Dear All,

Design code – ASME B31.3, Welding Code- ASME BPVC SEC IX

Material to be used used during Fabrication - SA 333Gr6 (P No.1 Gr. 1) To SA 350-LF2 (P No.1 Gr. 2)

Production Thickness range-5.54mm(Minimum)-9.53mm(Maximum)

PWHT – Nil
MDMT-= -45 Deg Cel.

Kindly give your valuable suggestions for applicability of PQR impact requirement for above details.
Pl.reply with code clause.
Thanks & Regards
Vinit
India

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/670487658.2039399.1713956840743%40mail.yahoo.com.

Best regards,

Amol K.B

B.E(Mech), CSWIP 3.2.2, NACE CIP 1 & ASNT LII(4M)

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAADcG1rM%2Bo7YWiYwxi2mV_AwQ0%2BvozmL7uPNM_uw3WCT1OaZqA%40mail.gmail.com.

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...

Materials & Welding

Search This Blog