Re: [MW:34509] ALUMINIUM 6082 -T6

u might used 5356 or 5556, 

THANKS & BEST REGARDS,

KG.PANDITHAN, BE, IWE,  CSWIP 3.1,

ISO 9712 Level 2 in VT,

ASNT-Level II in PT,MT,RT & UT,

LA ISO 9001-2015,

International Welding Engineer. 

CONSULTANT-WELDING & QUALITY

Mobile no: +919940739349

On Tue, Aug 22, 2023 at 9:30 AM Vishwas Keskar Welding Manager WELDING <vvkeskar123@gmail.com> wrote:

Dear Experts 

ALUMINIUM 6082 -T6 - 32mm , 20 mm , 16 mm plates 

32mm ,-32mm- Butt joint

 20 mm-20 mm-Butt joint

16 mm - 16 mm -Butt joint

Above plates are jointed through butt joints  .

Welding Process - GMAW 

Gas - Argon 

Filler wire  - ER4043

Due to job part length , there is distortion at the vicinity of butt welds. So Cold straightening operation was carried out on Press. The weld/HAZ cracking is observed  immediately the press load is commenced

Pl. suggest suitable action for Welding/cold straightening 

Thanks 

Vishwas - IWE

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/597ef31f-53c7-4c81-9924-cbbdd688c49an%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJzm4ePu3mUEPdaDkyrntUvhFzVN1FkFqCKdND3EjnDqUXCC8g%40mail.gmail.com.